310S stainless steel has good high temperature resistance. When the
temperature exceeds 800 ℃, it begins to soften, the allowable
stress begins to decrease continuously, and the maximum service
temperature is 1200 ℃. Due to the high content of nickel (Ni) and
chromium (CR), it has good oxidation resistance, corrosion
resistance, acid and alkali resistance and high temperature
resistance. High temperature resistant steel pipes are specially
used for manufacturing electric furnace tubes. After the carbon
content is increased in austenitic stainless steel, the strength is
improved due to its solid solution strengthening effect. The
chemical composition characteristics of austenitic stainless steel
are based on chromium and nickel, molybdenum, tungsten Niobium and
titanium have high strength and creep strength at high temperature
because of their face centered cubic structure.
Stainless Steel Strip Coils Grade 310S
3.5mm～1550mm or as required
0.02mm～40mm or as required
Hot rolled / cold rolled
2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, chequered, embossed,
hairline, sand blast, Brush, etching, Hot rolled plate (HR), Cold
rolled sheet (CR), SATIN (Met with Plastic Coated) etc
|310S stainless steel|
Petroleum, electronics, chemical industry, medicine, light textile,
food, machinery, construction, nuclear power, aerospace, military
industry and other industries.
1 ton , We can accept sample order.
Within 15-20 workdays after receiving deposit or workable L/C
Waterproof paper, and steel strip packed.
Standard Export Seaworthy Package.Suit for all kinds of
transport,or as required
Weight % (all values are maximum unless a range is otherwise
|C||0.25||0.08||0.40 min. - 0.10 max.|
|Cr||24.0 min.-26.0 max.||24.0 min.-26.0 max.||24.0 min.-26.0 max.|
|Ni||19.0 min.-22.0 max.||19.0 min.-22.0 max.||19.0 min.-22.0 max.|
Physical Properties :
|Density||Thermal Conductivity 212°F (100°C)|
|0.285 lbs/in3||8.0 BTU/hr/ft2/ft/°F|
|7.89 g/cm3||10.8 W/m-°K|
|Specific Heat||Melting Range|
|0.12 BTU/lb-°F (32 – 212°F)||2470 – 2555°F|
|502 J/kg-°K (0 – 100°C)||1354 – 1402°C|
|Modulus of Elasticity||Electrical Resistivity|
|28.5 x 106 psi||30.7 Microhm-in at 68°C|
|196 GPa||78.0 Microhm-cm at 20°C|
Typical Values at 68°F (20°C)
|Yield Strength||Ultimate Tensile||Elongation||Hardness|
|0.2% Offset||Strength||in 2 in.|
|psi (min.)||(MPa)||psi (min.)||(MPa)||% (min.)||(max.)|
Difference between 310 and 310S:
310 stainless steel has a relatively high carbon content of 0.25%,
while 310S stainless steel has a low carbon content of 0.08%, and
other chemical components are exactly the same. Therefore, 310
stainless steel has higher strength and hardness and poor corrosion
resistance. 310S stainless steel has better corrosion resistance
and slightly lower strength. 310S stainless steel is difficult to
smelt due to its low carbon content, so the price is relatively
Q1. What are your company's main products ?
A1: Our main products are stainless steel plate/sheet, coil,
round/square pipe, bar, channel, etc.
Q2. How do you control quality ?
A2: Mill Test Certification is supplied with shipment, Third Party
Inspection is available. and we also get ISO,SGS,Alibaba Verified.
Q3. What are the advantages of your company ?
A35: We have many professionals, technical personnel, more
competitive prices and best after-dales service than other
stainless steel companies.
Q4: What is the terms of packing?
A3: generally, we pack our goods in bundles or coils with rods or
belts, we could also pack the goods as the customers requirement.
Q5:What is your delivery time?
A4: For stocks, we could transport the goods to loading port within
7 days after we received your deposit
For production period, it usually takes about 15 days-30 days after
receiving the deposit.
Q6. Can you provide sample ?
A7: We can provide the samll samples in stock for free, as long as
you contact us.
Customized samples will take about 5-7days.
Q7. How many coutries you already exported ?
A6: Exported to more than 50 countries mainly from America, Russia,
UK, Kuwait, Egypt, Turkey, Jordan,India, etc.